Ultrafine-grained low carbon steels by severe plastic deformation (SPD)
Ultrafine-grained low carbon steels by severe plastic deformation (SPD) // 8. međunarodni simpozij Hrvatskog metalurškog društva "Materijali i metalurgija" : sažeci (tiskano u: Metalurgija 47(2008)3 (229-284)) / Mamuzić, Ilija (ur.).
Zagreb: Hrvatsko metalurško društvo, 2008. str. 227-227 (pozvano predavanje, međunarodna recenzija, sažetak, znanstveni)
CROSBI ID: 996864 Za ispravke kontaktirajte CROSBI podršku putem web obrasca
Naslov
Ultrafine-grained low carbon steels by severe plastic deformation (SPD)
Autori
Dobatkin, S. V. ; Zrnik, J. ; Mamuzić, Ilija
Vrsta, podvrsta i kategorija rada
Sažeci sa skupova, sažetak, znanstveni
Izvornik
8. međunarodni simpozij Hrvatskog metalurškog društva "Materijali i metalurgija" : sažeci (tiskano u: Metalurgija 47(2008)3 (229-284))
/ Mamuzić, Ilija - Zagreb : Hrvatsko metalurško društvo, 2008, 227-227
Skup
8. međunarodni simpozij Hrvatskog metalurškog društva "Materijali i metalurgija"
Mjesto i datum
Šibenik, Hrvatska, 22.06.2008. - 26.06.2008
Vrsta sudjelovanja
Pozvano predavanje
Vrsta recenzije
Međunarodna recenzija
Ključne riječi
Low carbon steel ; severe plastic deformation (SPD) ; equal channel angular pressing ; submicrocrystalline structure ; strength
Sažetak
The structure and properties of 0, 14% C and 0, 1% C - B low-carbon steels taken in two initial states, martensitic and ferritic-pearlitic, were studied after cold equal-channel angular (ECA) pressing. ECA pressing leads to the formation of only partially submicrocrystalline structure with a grain size of 150 – 300 nm, depending on the steel alloying and initial state. The finest structure with the elements of 190 nm in size is obtained in the 0, 1% C - B steel microalloyed with boron. The strength of the 0, 1% C - B steel after cold ECA pressing (Rm = 805-1235 MPa) meets the specifications of fasteners of the R80 - R120 strength grade. The strength of the deformed 0, 14% C steel is close to the R80 strength grade.