Research into possibilities of reducing the X155CrVMo12-1 tool steel fragility
Research into possibilities of reducing the X155CrVMo12-1 tool steel fragility // Metalurgija, 57 (2018), 4; 330-332 (međunarodna recenzija, članak, znanstveni)
CROSBI ID: 945300 Za ispravke kontaktirajte CROSBI podršku putem web obrasca
Naslov
Research into possibilities of reducing the X155CrVMo12-1 tool steel fragility
Autori
Marušić, Vlatko ; Milinović, Andrijana ; Opačak, Ivan ; Putnik, Ivan
Izvornik
Metalurgija (0543-5846) 57
(2018), 4;
330-332
Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni
Ključne riječi
X155CrVMo12-1 steel ; fragility ; cracks ; structure ; hardness
Sažetak
This research varies the parameters of austenitization and quenching of the tool steel X155CrVMo12-1. It also focuses on investigation of the structure, hardness and impact energy. It was determined that the cracks were generally intercrystalline, with carbide deposition. It was observed that quenching at the temperature interval from ≈ 700 °C to ≈ 600 °C, at a speed greater than 15 °C/s, achieved higher impact energy with about the same hardness. It was concluded that prevention of carbide coalescence had influence on the reduction of steel fragility.
Izvorni jezik
Engleski
Znanstvena područja
Strojarstvo
POVEZANOST RADA
Ustanove:
Strojarski fakultet, Slavonski Brod
Citiraj ovu publikaciju:
Časopis indeksira:
- Web of Science Core Collection (WoSCC)
- Emerging Sources Citation Index (ESCI)
- Scopus