Naslov
Surface quality of the Ni-TiO2 Composite coatings produced by electroplating

Autori
Stanković, Velizar ; Gojo, Miroslav ; Grekulović, Vesna ; Pajkić, Ninoslav ; Cigula, Tomislav

Izvornik
Journal of mining and metallurgy. Section: B, Metallurgy (1450-5339) 53 (2017), 3; 341-348

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
Nickel electroplating ; TiO2 particles ; Composite coatings ; Surface roughness ; Surface profilograms

Sažetak
Composite nickel coatings on a brass substrate were produced from suspensions consisted of a conventional nickel sulphate bath and fine TiO2 particles (dp < 0.35 µm). Characterization of coatings surface was performed by using optical and SEM micrographs, by EDS analysis and by determining the surface roughness parameters. Metallographic analysis has also been done in order to get an insight about particles distribution throughout the thickness of the coating layer. Presence of TiO2 particles in electrodeposited metal affected the surface morphology. Particles were embedded as smaller or bigger agglomerates within the coatings, as well as the individual particles. Metallographic analysis showed uniform distribution of particles and their agglomerates within the coating. Surface roughness parameters of the composites have had up to 35 times higher values than the ones of the pure nickel coatings. Roughness maxima appeared at the concentration of particles between 10 and 20 g dm-3. Then it drops down and remains constant for concentrations > 40 gdm-3. SEM micrographs showed irregularities like single-nodule, or beads of nodules on the surface. Relationship between surface roughness and current density has not been noted.

Izvorni jezik
Engleski

Znanstvena područja
Kemijsko inženjerstvo, Interdisciplinarne tehničke znanosti

POVEZANOST RADA