Characterization of Ag and Au nanolayers on Cu alloys by TLC, SEM-EDS, and ICP-OES

Autori
Rezić, Iva ; Špehra, Martina ; Jakovljević, Suzana

Izvornik
Materials and corrosion (0947-5117) 68 (2017), 5; 560-565

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
nanolayers ; silver ; gold ; spectroscopy

Sažetak
This paper reports a study on four historical samples from 19th century originating from Croatia, Europe, made of silver plated and gilded copper alloys. The investigation was carried out by chromatographic, spectroscopic, and microscopic techniques. Corrosion was identified in all samples by scanning electron microscope-energy dispersive spectroscopy (SEM-EDS), although the samples were in well-preserved states. EDS has given the following average composition of elements Ag (82.99, 4.74, 6.34, and 15.54wt% in samples 1–4, respectively), Au (17.01wt%in sample 1), and Cu(0, 95.26, 93.66, and 84.46 wt% in samples 1–4, respectively) for theouter layers of the samples.The exactsample elemental composition was determined by inductively coupled plasma optical emission spectroscopy (ICP-OES): 0.12, 0.22, 0.68, and 1.20wt% Ag in samples 1–4, respectively and 0.02wt%Au in sample 2, all on Cu alloyswith impurities of Fe, Mn, Ni, Pb, Sb, Si, Sn, and Zn (in quantities 0.05–1.48 wt%). Preliminary detection of metals was performed by thin-layer chromatography. Results of determined chemical composition were consistent with similar investigations, since silver-plated and gilded Cu alloyswere thematerials used in the production of similar samples through the history.

Izvorni jezik
Engleski

POVEZANOST RADA