Erosion resistance of slip cast composite Al2O3- ZrO2 ceramics

Autori
Majić Renjo, Marijana, Ćurković, Lidija, Grilec, Krešimir

Vrsta, podvrsta i kategorija rada
Radovi u zbornicima skupova, cjeloviti rad (in extenso), znanstveni

Izvornik
The 25th DAAAM International Symposium Intelligent Manufacturing & Automation / - , 2014

Skup
The 25th DAAAM International Symposium Intelligent Manufacturing & Automation

Mjesto i datum
Beč, Austrija, 26.11.2014. - 29.11.2014

Vrsta sudjelovanja
Predavanje

Vrsta recenzije
Međunarodna recenzija

Ključne riječi
alumina (Al2O3); zirconia (ZrO2); Al2O3–ZrO2 composite ceramics; erosion resistance; slip casting

Sažetak
In this paper, erosion resistance of slip cast monolithic (Al2O3) and composite (Al2O3–t-ZrO2) ceramics was investigated by dry silica sand (SiO2) erodent. The amount of t-ZrO2 in powder mixture of Al2O3–t-ZrO2 was 5 wt. % and 10 wt. %. The erosive wear behaviour was studied at following impact angles of erodent: 30°, 60° and 90°. Erosion mechanisms of all prepared ceramic samples were evaluated by measuring the roughness parameters (Ra, Rz, Rmax) and weight loss, as well as analysis of surface morphology by means of scanning electron microscope (SEM). Obtained results showed that tribological properties of monolithic Al2O3 can be improved with the addition of t-ZrO2. It was also found that erosion resistance increases with the increasing amount of t-ZrO2 in the powder mixture. Generally, for all investigated ceramic samples erosion resistance decreases by the increasing erodent impact angle.