High-transport critical current density above 30 K in pure Fe-clad MgB2 tape

Autori
Soltanian, S. ; Wang, X. L. ; Kušević, Ivica ; Babić, Emil ; Li, A. H. ; Qin, M. J. ; Horvat, Joža ; Liu, H. K. ; Collings, E. W. ; Lee, E. ; Sumption, M. D. ; Dou, Shi Xue

Izvornik
Physica C (0921-4534) 361 (2001); 84-90

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
magnesium boride;critical current density;iron cladding;superconductor

Sažetak
Fe-clad MgB2 long tapes have been fabricated using a powder-in-tube technique. An Mg + 2B mixture was used as the central conductor core and reacted in-situ to form MgB2. The tapes were sintered in pure Ar at 800 o C for 1 h at ambient pressure. SEM shows a highly dense core with a large grain size of 100 microm. The Fe-clad tape shows a sharp transition with transition width of deltaTc of 0.2 K and Tc0 at 37.5 K. We have achieved the highest transport critical current reported so far at 1.7 x10^4 A/cm^2 for both 29.5 K in 1 Tesla and 33 K in zero applied field. Resistivity temperature dependence and transport critical current were also measured in magnetic fields applied perpendicular and parallel to the tape plane. Not only is the use of an Fe sheath necessary for the successful processing of in situ reacted powder-in-tube MgB2, it confers on the finished wire the additional benefit of magnetic screening.

Izvorni jezik
Engleski

Znanstvena područja
Fizika

POVEZANOST RADA