Naslov
The Effect of Long-Term Annealing at Elevated Temperature on Microstructure and Hardness of Heat-Resistant Steel

Autori
Kosec, Ladislav ; Gojić, Mirko ; Kožuh, Stjepan ; Kosec, Borut ; Dražić, Goran ; Šavli, Štefan

Izvornik
Materials science forum (1662-9752) 782 (2014); 209-214

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
heat-resistant steel ; annealing ; sigma phase ; hardness ; fracture surface

Sažetak
The stainless steel group AISI 310 is very often used for application in high-temperature conditions. This study investigated the effect of long-term annealing on microstructure and hardness of AISI 310S (24.3% Cr-19.3% Ni – 1.8% Mn – 0.21% Mo – 0.67% Si, wt.%) heat-resistant steel. Microstructural changes and hardness distribution were analyzed after isothermal annealing at 800 °C in long-term exposure (from 1 to 1740 hours). Microstructure and fracture surface mode were analyzed using scanning electron microscopy (SEM) equipped with energy dispersive X-ray spectroscopy (EDS). It was found that after annealing the sigma phase particles were precipitated at grain boundaries and within austenite grains. The chromium content in the sigma phase increased with the prolongation of annealing time. The morphology of sigma phase was changed from fine precipitates at lower annealing times to coarser particles at higher annealing times. Also, presence of sigma phase was confirmed by transmission electron microscopy (TEM). At annealing temperature of 800 °C the hardness began to increase after 16 hours. With longer times of annealing the fracture surfaces were changed. This change is associated with a change of content and the morphology of sigma phase.

Izvorni jezik
Engleski

Znanstvena područja
Metalurgija

POVEZANOST RADA