Naslov
Comparison of corrosion products formed on black and corrosion resistant steel reinforcement embedded in cement paste

Autori
Serdar, Marijana ; Bjegovic, Dubravka ; Meral, Cagla ; Monteiro, Paulo

Vrsta, podvrsta i kategorija rada
Radovi u zbornicima skupova, cjeloviti rad (in extenso), znanstveni

Izvornik
Eurocorr 2012 / European Federation of Corrosion - Istanbul : European Federation of Corrosion, 2012, 240-240

Skup
Eurocorr 2012 - Safer world through better corrosion control

Mjesto i datum
Istanbul, Turska, 09.09.2012. - 13.09.2012

Vrsta sudjelovanja
Predavanje

Vrsta recenzije
Međunarodna recenzija

Ključne riječi
corrosion resistant steel; concrete; corrosion products; SEM; EIS

Sažetak
Present research compares morphology and composition of corrosion products formed during accelerated corrosion of black and corrosion resistant steel embedded in ordinary cement paste. For this purpose, cement paste samples with different types of embedded steel were cast and cured. After curing, samples were placed in to 3.5% NaCl solution to simulate marine environment exposure. During this period samples were kept under constant potential of 500 mV vs SCE. When a significant increase in current was reached, samples were removed from the solution. The formed corrosion products in the steel/cement paste interface were investigated through scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS) and X-ray diffraction (XRD). Analysis of corrosion products showed that depending on the chemical composition of the reinforcing steel, different corrosion products were formed around different types of steel. Morphology and chemical composition of the corrosion products changed with the amount of Cr present in the steel. Based on these results, a pattern of formation of corrosion products during corrosion of stainless steel in concrete was proposed.