Primjena niskotemperaturnog aluminiziranja kod čelika za topli rad
Primjena niskotemperaturnog aluminiziranja kod čelika za topli rad // International conference Heat treatment and surface engineering - European opportunities for Croatian economy : proceedings book = Međunarodno savjetovanje Toplinska obrada i inženjerstvo površina - europske mogućnosti hrvatskog gospodarstva : zbornik radova / Smoljan, Božo ; Iljkić, Dario (ur.).
Rijeka: Hrvatsko društvo za toplinsku obradu i inženjerstvo površina, 2012. str. 51-56 (predavanje, međunarodna recenzija, cjeloviti rad (in extenso), znanstveni)
CROSBI ID: 580918 Za ispravke kontaktirajte CROSBI podršku putem web obrasca
Naslov
Primjena niskotemperaturnog aluminiziranja kod čelika za topli rad
(Application of low temperature aluminizing on hot work tool steels)
Autori
Matijević ; Božidar
Vrsta, podvrsta i kategorija rada
Radovi u zbornicima skupova, cjeloviti rad (in extenso), znanstveni
Izvornik
International conference Heat treatment and surface engineering - European opportunities for Croatian economy : proceedings book = Međunarodno savjetovanje Toplinska obrada i inženjerstvo površina - europske mogućnosti hrvatskog gospodarstva : zbornik radova
/ Smoljan, Božo ; Iljkić, Dario - Rijeka : Hrvatsko društvo za toplinsku obradu i inženjerstvo površina, 2012, 51-56
ISBN
978-953-7690-03-8
Skup
Međunarodno savjetovanje Toplinska obrada i inženjerstvo površina - europske mogućnosti hrvatskog gospodarstva
Mjesto i datum
Rijeka, Hrvatska, 11.05.2012
Vrsta sudjelovanja
Predavanje
Vrsta recenzije
Međunarodna recenzija
Ključne riječi
aluminiziranje; reaktivno nataljenje; erosija; tlačni lijev
(aluminising; reactive soldering; erosion; die casting)
Sažetak
During die-casting of aluminium components, tool parts are exposed to a complex combination of different wear mechanisms, such as thermal fatigue, erosion and reactive soldering of the die surfaces. As a result, this causes damage and severely reduces the durability of tools, thus increasing tools maintenance costs. For increased resistance to reaction soldering, different methods of thermo-chemical surface modification techniques (such as nitriding or vanadising) or different processes of coatings may be applied. In this paper, the possibility of using low-temperature, low-potential aluminizing with subsequent oxidation of aluminized hot work tool steel surface has been explored. In this case, formation of stable and compact aluminium oixide (Al2O3) layer is what prevents direct contact of molten metal with the base die alloy, making it resistant (to some extent) to reaction soldering.
Izvorni jezik
Hrvatski
Znanstvena područja
Kemijsko inženjerstvo, Metalurgija, Strojarstvo
POVEZANOST RADA
Projekti:
120-1201833-1791 - Inženjerstvo površina u proizvodnji konstrukcijskih dijelova i alata (Cajner, Franjo, MZOS ) ( CroRIS)
120-1252973-1814 - Difuzijsko modificiranje čelika karbidnim slojevima (Matijević, Božidar, MZOS ) ( CroRIS)
Ustanove:
Fakultet strojarstva i brodogradnje, Zagreb
Profili:
Božidar Matijević
(autor)