Some influential parameters on porosity defects in casting of Al ingot castings
Some influential parameters on porosity defects in casting of Al ingot castings // Metalurgija, 38 (1999), 4; 227-231 (međunarodna recenzija, članak, znanstveni)
CROSBI ID: 54126 Za ispravke kontaktirajte CROSBI podršku putem web obrasca
Naslov
Some influential parameters on porosity defects in casting of Al ingot castings
Autori
Budić, Ivan ; Bonačić-Mandinić, Zoran
Izvornik
Metalurgija (0543-5846) 38
(1999), 4;
227-231
Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni
Ključne riječi
foundry; casting defects of aluminium; porosity
Sažetak
A major problem in foundry industry is porosity. Porosity formation is a complex phenomena still lacking in thorough and detailed insight, which explains why this problem has been so frequently studied nowadays. This paper studies the causes for this serious casting defect: metal static height, pouring temperatures, influence of moisture level in the sand core on porosity of aluminum alloy AlSi12 poured in metal mold. The results purport to significance of parameters to porosity.
Izvorni jezik
Engleski
Znanstvena područja
Strojarstvo
Citiraj ovu publikaciju:
Časopis indeksira:
- Web of Science Core Collection (WoSCC)
- Science Citation Index Expanded (SCI-EXP)
- SCI-EXP, SSCI i/ili A&HCI
- Scopus