Tribocorrosion of low carbon steel C15E IN 5%NaCl and 5%NaCl + SiO<sub>2</sub>
Tribocorrosion of low carbon steel C15E IN 5%NaCl and 5%NaCl + SiO2 // Sažeci predavanja s 9. međunarodnog simpozija Hrvatskog metalurškog društva SHMD '2010. "Materijali i metalurgija", tiskano u Metalurgija 49 (2010) 3 / Mamuzić, Ilija (ur.).
Zagreb: Hrvatsko metalurško društvo, 2010. str. 200-200 (poster, međunarodna recenzija, sažetak, znanstveni)
CROSBI ID: 493674 Za ispravke kontaktirajte CROSBI podršku putem web obrasca
Naslov
Tribocorrosion of low carbon steel C15E IN 5%NaCl and 5%NaCl + SiO<sub>2</sub>
(Tribocorrosion of low carbon steel C15E IN 5%NaCl and5%NaCl + SiO<sub>2</sub>)
Autori
Aračić, Stjepan ; Krumes, Dragomir ; Vitez, Ivan
Vrsta, podvrsta i kategorija rada
Sažeci sa skupova, sažetak, znanstveni
Izvornik
Sažeci predavanja s 9. međunarodnog simpozija Hrvatskog metalurškog društva SHMD '2010. "Materijali i metalurgija", tiskano u Metalurgija 49 (2010) 3
/ Mamuzić, Ilija - Zagreb : Hrvatsko metalurško društvo, 2010, 200-200
Skup
9. međunarodni simpozij Hrvatskog metalurškog društva "SHMD '2010. : Materijali i metalurgija"
Mjesto i datum
Šibenik, Hrvatska, 20.06.2010. - 24.06.2010
Vrsta sudjelovanja
Poster
Vrsta recenzije
Međunarodna recenzija
Ključne riječi
low carbon steel
Sažetak
The article represents testing results of corrosion and erosion-corrosion wear. Specimens have been made from low carbon steel C15E in four different states: delivery state and heat-treated (carburizing, boronising and carburizing + boronising). The results are shown as wear of materials (losing of surface mass in mg/(cm<sup>2</sup>×d)). Surface hardness method HV1 and micro hardness per section of specimen HV0, 2 method have been used during the analyses. A comparison of testing results of wear in four different states was made. The best performances have shown samples which have been treated with duplex procedure (carburizing + boronising) as was predicted.
Izvorni jezik
Engleski
Znanstvena područja
Metalurgija, Strojarstvo
POVEZANOST RADA
Projekti:
120-1201787-1491 - Oblikovanje deformiranjem i svojstva novih metalnih materijala (Mamuzić, Ilija, MZOS ) ( CroRIS)
152-1201833-1471 - Utjecaj duplex postupka na strukturu čelika i inženjerstvo površina (Krumes, Dragomir, MZOS ) ( CroRIS)
Ustanove:
Strojarski fakultet, Slavonski Brod