Naslov
Niobium doped TiO2 with mesoporosity and its application for lithium battery

Autori
Wang, Yude ; Smarsly, Bernd ; Djerdj, Igor

Izvornik
Chemistry of materials (0897-4756) 22 (2010), 24; 6624-6631

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
lithium-ion battery; mesoporous; doped

Sažetak
The synthesis as well as the electrochemical properties study of niobium-doped TiO2 (NTO) with mesoporosity and high surface area is presented. The mesoporous NTO was prepared using a novel poly(ethylene-co-butylene)-b-poly(ethylene oxide) amphiphilic diblock copolymer as template and simple titanium reagents (TiCl4 and Nb(OC2H5)5) by a polymer-assisted sol-gel process. The samples were characterized by differential scanning calorimetry and thermogravimetric analysis (DSC-TGA), X-ray diffraction (XRD), Fourier transformed infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), transmission electron microscopy (including high-resolution imaging-HRTEM), and the Brunauer–Emmett–Teller (BET). All samples are highly crystalline and have pore-solid architectures after removal of the polymer template by calcination. The resulting mesoporous NTO shows a high porosity of 46 % and a high surface area of 128 m2/g, respectively. The as-prepared samples were used as positive electrode materials for lithium–ion battery, whose charge–discharge properties, cyclic voltammetry, and cycle performance were examined and revealed very good properties. A highly stable capacity of 160 mA h g-1 was found after 100 cycles.

Izvorni jezik
Engleski

Znanstvena područja
Fizika

POVEZANOST RADA