Naslov
The influence of thermal treatment on the performance of Ni/Al2O3 catalyst

Autori
Tomašić, Vesna ; Geržina, Anica ; Zrnčević, Stanka

Izvornik
Chemical and biochemical engineering quarterly (0352-9568) 14 (2000), 2; 47-52

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
thermal treatment (calcination) ; thioresistance of Ni/Al2O3 catalyst ; calcination ; benzene hydrogenation ; kinetics of dectivation

Sažetak
The data showing the influence of calcination conditions on physical and catalitic properties of Ni/Al2O3 catalyst, are presented and discussed. The catalst characterization was performed by X-ray diffraction analysis and adsorption of nitrogen at 77 K. Activity of the Ni/Al2O3 catalyst was tested using benzene hydrogenation in the presence of thiophene as poisoning molecule. It has been found that the calcination temperature directly influenced physico-chemical properties responsible for thioresistance of NiAl2O3 catalyst, whereas calcination time had little effect on the catalytic properties of catalyst. The crystallite size of NiO and of the support particles incresed with the elevation of calcination temperature from 573 to 873 K, while the surface area of the catalyst decreased. Benzene conversion was higher, and the catalyst deactivation due to thiophene poisoning, was slower, when the crystallites were smaller. That indicated, that both reaction, i.e. benzene hydrogenation and catalyst poisoning by thiophene, were structure-sensitive and that calcination at 873 K probably led to modification of electronic properties of the catalytic active sites. At the same time, higher resistance to thiophene poisoning may prolong the catalyst lifetime.

Izvorni jezik
Engleski

Znanstvena područja
Kemijsko inženjerstvo

POVEZANOST RADA