Thermal Properties of Alkyl-modified Phenyl- silsesquioxanes

Autori
Macan, Jelena ; Tadanaga, Kiyoharu ; Tatsumisago, Masahiro

Vrsta, podvrsta i kategorija rada
Sažeci sa skupova, sažetak, znanstveni

Izvornik
XXI. Hrvatski skup kemičara i kemijskih inženjera – Knjiga sažetaka / Novak, Predrag ; Pičuljan, Katarina ; Smolec, Sonja - Zagreb : Hrvatsko društvo kemijskih inženjera i tehnologa (HDKI), 2009

ISBN
978-953-6894-38-3

Skup
XXI. hrvatski skup kemičara i kemijskih inženjera

Mjesto i datum
Trogir, Hrvatska, 19.04.2009. - 22.04.2009

Vrsta sudjelovanja
Poster

Vrsta recenzije
Nije recenziran

Ključne riječi
polysilsesquioxanes; thermal properties; sol-gel

Sažetak
Phenyl-silsesquioxanes are hybrid organic- inorganic compounds that can thermally soften, and whose softening temperature depends on the level of condensation, which can be controlled by conditions of synthesis [1]. Phenyl-silsesquioxane particles find application in preparation of transparent thick films or matrices for functional thin films. Other polysilsesquioxanes also can have softening temperature, which has been shown to depend on the size of organic supstituent [2]. In order to control the softening temperature and thermal stability of the phenyl-silsesquioxane particles, they were modified with alkyl chains of varying lengths. Polysilsesquioxane hybrid particles were prepared by two-step acid-base catalysed sol-gel process, with ethanol as solvent. Alkyl-triethoxysilanes, R-Si(OC2H5)3, R = CH3, C2H5, C5H11 and C8H17, were mixed with phenyl-triethoxysilane, C6H5-Si(OC2H5)3, in a constant 1:4 ratio, hydrolysed with aqueous solution of HCl and then condensed with aqueous solution of NH4OH. Resulting particles were dried, investigated by scanning electron microscopy, differential scanning calorimetry and combined differential thermal and thermogravimetric analysis. Pentyl- and octyl- modified particles were found to have less homogeneous size distribution, presumably because long alkyl chains were less miscible with other components resulting in less homogeneous initial mixture. Increased size of alkyl chains also presents greater sterical hindrance to condensation of phenyl- silsesqui-oxanes, so the softening temperature decreases from 380 °C for methyl-modified particles to 50-100 °C for octyl-modified ones. Thermal stability of alkyl-modified particles was expected to decrease, since alkyl-silsesquioxanes degrade at much lower temperatures. Methyl- and ethyl-modified particles start to degrade at 400 °C, same as unmodified phenyl-silsesquioxane, while pentyl- and octyl-modified particles start to degrade at 250 °C, which corresponds to degradation of pentyl- and octyl-silsesquioxanes. Therefore it can be supposed that longer alkyl chains are exposed on the surface of the particles while shorter ethyl and methyl groups are in some way shielded by phenyl groups.