Naslov
Influence of thermal oxides on pitting corrosion of austenitic and duplex steels

Autori
Alar, Vesna ; Rede, Vera ; Juraga, Ivan ; Runje, Biserka

Vrsta, podvrsta i kategorija rada
Poglavlja u knjigama, znanstveni

Knjiga
Passivation of metals and semiconductors, and properties of thin oxide layers

Urednik/ci
Marcus, Philippe ; Maurice, Vincent

Izdavač
Elsevier

Grad
Amsterdam

Godina
2006

Raspon stranica
585-590

ISBN
978-0-444-52224-5

Ključne riječi
thermal oxides, austenitic, duplex, pitting

Sažetak
The influence of thermal oxides on pitting corrosion of austenitic and duplex (austenitic-ferrite) steels has been studied. Austenitic steel specimens AISI 316L were subjected to heating isothermally (200 to 1000°C) in order to simulate conditions of the application in production. Duplex steel specimens AISI S31803 were heated isothermally at (1100 to 1300°C) in order to simulate welding parameters. The characterization of thermal oxides formed by heating isothermally on austenitic steel was performed by AES, and XPS analyses. The microstructures and thickness of thermal oxides on austenitic specimens and microstructures on duplex specimens was determined. Pitting susceptibility of such specimens was tested by exposure to FeCl3 solution at 22&plusmn ; 2°C during 72h (ASTM G 48-99a). Pitting criteria show that oxides developed at 600°C cause the highest susceptibility to pitting corrosion for austenitic steel and 1300°C for duplex steel.