Diffusion during annealing of Al/Cu/Fe thin films

Autori
Čekada, Miha ; Panjan, Peter ; Dolinšek, Janez ; Zalar, Anton ; Medunić, Zvonko ; Jakšić, Milko ; Radić, Nikola

Izvornik
Thin Solid Films (0040-6090) 515 (2007), 18; 7135-7139

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
diffusion; Rutherford backscattering spectroscopy; Auger electron spectroscopy; Al-Cu-Fe

Sažetak
The Al-Cu-Fe system is interesting due to the existence of the quasicrystalline phase Al62.5Cu25Fe12.5 as well as its approximant phases. A two-step procedure of thin film preparation is considered: deposition of a multilayer structure of individual elements and consequential annealing. To analyze the diffusion processes trilayers of individual elements were deposited by sputtering with a total thickness of about 400 nm. Afterwards, the samples were annealed in tube furnace in inert atmosphere. Rutherford backscattering spectrometry, Auger electron spectrometry and X-ray diffraction were used to quantify the depth profiles. The results point out to a three-stage process as a function of rising temperature: first Al and Cu form the γ -Al4Cu9 compound layer ; second the aluminium spreads throughout the film with copper and iron mainly divided. The β -Al(Cu, Fe) phase is observed. Complete homogenization is followed afterwards.

Izvorni jezik
Engleski

Znanstvena područja
Fizika

POVEZANOST RADA