PERFORMANCE OF LOW-SILICON VACUUM REMELTED HOT WORK TOOL STEEL UNDER HIGH THERMAL LOAD
PERFORMANCE OF LOW-SILICON VACUUM REMELTED HOT WORK TOOL STEEL UNDER HIGH THERMAL LOAD // PROCEEDINGS OF 7TH INTERNATIONAL TOOLING CONFERENCE / MARIO, ROSSO, M. ACTIS, GRANDE, DANIEL, UGUES (ur.).
Torino: POLITECNICO DI TORINO, 2006. str. 191-198 (predavanje, međunarodna recenzija, cjeloviti rad (in extenso), znanstveni)
CROSBI ID: 270183 Za ispravke kontaktirajte CROSBI podršku putem web obrasca
Naslov
PERFORMANCE OF LOW-SILICON VACUUM REMELTED HOT WORK TOOL STEEL UNDER HIGH THERMAL LOAD
Autori
Goršćak, Đurđica ; Leskovšek, Vojteh ; Godec, M. ; Vujnović, Srećko ; Kapuđija, D. ; Ćurković, Lidija
Vrsta, podvrsta i kategorija rada
Radovi u zbornicima skupova, cjeloviti rad (in extenso), znanstveni
Izvornik
PROCEEDINGS OF 7TH INTERNATIONAL TOOLING CONFERENCE
/ MARIO, ROSSO, M. ACTIS, GRANDE, DANIEL, UGUES - Torino : POLITECNICO DI TORINO, 2006, 191-198
Skup
TOOLING MATERIALS AND THEIR APPLICATIONS FROM RESEARCH TO MARKET
Mjesto i datum
Torino, Italija, 02.05.2006. - 05.05.2006
Vrsta sudjelovanja
Predavanje
Vrsta recenzije
Međunarodna recenzija
Ključne riječi
aluminium alloy die casting mould; heat checking resistance; hot strength
Sažetak
Exploitation of the critical parts in die casting moulds for radiators was observed for years and it was found that dominant wear mechanism was heat checking. After 1.2343 and 1.2367 grades, a vacuum remelted grade,  1.2343 with a lowered silicon content was used. At hardness of ca. 44 HRC, lifetime of the critical mould part significantly decreased, where heavy cracks occured. Notched impact energy and metallography of the mould part samples were analyzed.