Sinteza forsterita iz aluminosilikatnih prekursora
(Synthesis of Forsterite from Aluminosilicate Precursors)

Autori
Kosanović, Cleo ; Tomašić, Nenad ; Stubičar, Mirko ; Gajović, Andreja

Vrsta, podvrsta i kategorija rada
Sažeci sa skupova, sažetak, znanstveni

Izvornik
Knjiga sažetaka = Book of abstracts / XIX. hrvatski skup kemičara i kemijskih inženjera / Rapić, Vladimir ; Rogošić, Marko - Zagreb : Hrvatsko društvo kemijskih inženjera i tehnologa (HDKI) ; Hrvatsko kemijsko drustvo, 2005, 371-371

Skup
XIX. hrvatski skup kemičara i kemijskih inženjera

Mjesto i datum
Opatija, Hrvatska, 24.04.2005. - 27.04.2005

Vrsta sudjelovanja
Poster

Vrsta recenzije
Međunarodna recenzija

Ključne riječi
Forsterit; Priprava; Smjesa NH4-izmjenjeni Zeolit A i MgO; Smjesa NH4-izmjenjeni mordenit i MgO; Intenzivno kuglično mljevenje; Toplinska obrada; Rentgenska difrakcija; FT-IR spektroskopija; Raman spektroskopija.
(Forsterite; Synthesis; Mixture of NH4-exchanged Zeolite A and MgO; Mixture of NH4-exchanged mordenite and MgO; High-energy ball milling; Heat treatment; X-Ray diffraction; FT-IR spectroscopy; Raman spectroscopy.)

Sažetak
Using as starting materials the powder mixture of NH4-exchanged zeolite A and MgO, and powder mixture of NH4-exchanged mordenite and MgO, crystalline ceramic materials were obtained [1]. In order to produce a homogeneous mixture, conventional ball milling was applied causing the amorphization of NH4-exchanged zeolites and reduction of the particle size of MgO [2]. Solid-state transformation of the mixtures after heating at temperature of their phase transformations in the interval of 800oC-1000oC for 3 h yielded crystalline forsterite (Mg2SiO4) with possibly minor amounts of sapphirine (Mg4Al10Si2=23) and spinel (MgAl2O4) in the first case, and crystalline forsterite with traces of enstatite (MgSiO3) in the second case. X-ray diffraction [3], FT-IR spectroscopy [4] and Raman spectroscopy [5] were used for the product characterization.