High Temperature Strength of Niobium Alloy 5VMTs with a Silicide Ceramic Coating, Part1. Short Term Strength Characteristics
High Temperature Strength of Niobium Alloy 5VMTs with a Silicide Ceramic Coating, Part1. Short Term Strength Characteristics // Strength of materials, 36 (2004), 2; 119-129 (međunarodna recenzija, članak, znanstveni)
CROSBI ID: 153825 Za ispravke kontaktirajte CROSBI podršku putem web obrasca
Naslov
High Temperature Strength of Niobium Alloy 5VMTs with a Silicide Ceramic Coating, Part1. Short Term Strength Characteristics
Autori
Bukhanovski, V. ; Borisenko, A. ; Kharchenko, K. ; Mamuzić, Ilija
Izvornik
Strength of materials (0039-2316) 36
(2004), 2;
119-129
Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni
Ključne riječi
niobium alloy ; silicide-ceramic protective coating ; composite ; high temperatures load-carryng capacity
Sažetak
Experimental dana on the short-term strength and plasticity of niobium alloy 5VMTs of the system Nb-W-Mo-Zr in its initial state, after annealing, and with a silicide-ceramic protective coating obtained by testing in vacuum, an inter atmosphere, and in air in the temperature range from 290 to 2270 K are analyzed. The process of microcrack initiation and propagation in the protective coating and matrix is investigated in high-temperature static tension. The limiting plastic strain values have been established at which the composite retains its load-carrying capacity in high-temperature aggressive and oxidizing gas atmospheres.
Izvorni jezik
Rus
Znanstvena područja
Metalurgija
POVEZANOST RADA
Citiraj ovu publikaciju:
Časopis indeksira:
- Scopus
Uključenost u ostale bibliografske baze podataka::
- Referativny Zhurnal