Thermooxidative degradation of poly(vinyl chloride)/chlorinated polyethylene blends investigated by thermal analysis methods

Autori
Stipanelov Vrandečić, Nataša ; Klarić, Ivka ; Kovačić, Tonka

Izvornik
Polymer Degradation and Stability (0141-3910) 84 (2004), 1; 23-30

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
Differential scanning calorimetry; Polymeric modifiers; PVC/CPE blends; Thermogravimetry; Thermooxidative degadation

Sažetak
The thermooxidative degradation of poly(vinyl chloride)/chlorinated polyethylene (PVC/CPE) blends of various compositions was investigated by means of thermal analysis methods: differential scanning calorimetry (DSC) and thermogravimetry (TG). By using DSC it was found that all investigated PVC/CPE blends were heterogenous. The main reaction of PVC degradation at moderate temperatures is dehydrochlorination, which is also dominant reaction in CPE degradation. In spite of chemical similarity of the investigated polymers, thermooxidative stability and degradation mechanism are different. In order to evaluate the effect of CPE on the thermooxidative degradation of PVC in the blends, different criteria have been used. It was found that CPE had the stabilizing effect on thermooxidative degradation of PVC and interactions of blends components with their degradation products occurred.

Izvorni jezik
Engleski

Znanstvena područja
Kemijsko inženjerstvo

POVEZANOST RADA