Influence aging temperature on tensile strength and elongation aluminium alloys 6060 and 6005A

Autori
Berić, Nikolina ; Stojšić, Josip ; Papić, Luka ; Marušić, Ante

Vrsta, podvrsta i kategorija rada
Radovi u zbornicima skupova, cjeloviti rad (in extenso), stručni

Izvornik
MTECH 2021 / Cindrić, Ivan ; Janković, Lara ; Kurtela, Marin - Zagreb : Hrvatsko društvo za zaštitu materijala (HDZaMa), 2021, 376-384

Skup
3rd International Conference on Materials: corrosion, heat treatment, materials testing and tribology (MTECH 2021)

Mjesto i datum
Šibenik, Hrvatska, 06.10.2021. - 09.10.2021

Vrsta sudjelovanja
Poster

Vrsta recenzije
Međunarodna recenzija

Ključne riječi
aluminium alloys, precipitation hardening, aging parameters, tensile strength, elongation

Sažetak
This work investigated the influence of aging temperature on the mechanical properties of 6000 series aluminum alloys. Solution annealing and aging of alloys 6060 (AlMgSi) and 6005 A [AlSiMg (A)] were performed. Test specimens were produced for the tensile test. All specimens were dissolved at the same parameters (530 °C/30min). Then, the samples were aged for 10 hours, varying the temperatures (160, 175 and 190 °C). After the aging procedure, a tensile test was performed on these samples and on a non-heat-treated sample to compare the results obtained. After the test, the analysis showed that the tensile strength and elongation of the old samples increased in relation to the non-heat-treated sample. The results of the tensile strength and elongation of the old samples show that for the same duration, the highest tensile strength and elongation were obtained at an aging temperature of 175 °C.