Effects of Photo-oxidation on the Properties of Hemp Office Papers

Autori
Plazonić, Ivana ; Džimbeg-Malčić, Vesna ; Bates, Irena ; Barbarić-Mikočević, Željka

Izvornik
International Journal of Technology (2086-9614) 11 (2020), 2; 215-224

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
Accelerated aging ; Hemp ; Office paper ; Xenon light source

Sažetak
This research observes changes in the properties of commercially available hemp office papers exposed to photo-oxidation for artificial aging. In order to accelerate the changes that naturally occur in paper, photo-oxidation was performed using a Xenon light source. The electromagnetic radiation was administered in doses of 550 W/m2 over 24 hours with a temperature of 60°C. Three types of hemp office papers that differ in chemical composition and manufacturing process were used as samples. The strength properties (tensile index, elongation at break, tear index), surface properties (Bendtsen roughness, Bekk smoothness), pH of paper extracts, and optical properties were observed. The listed properties of artificially aged samples were compared to those of unaged commercial paper samples. The results show that, after only 24 hours, accelerated aging with a Xenon arc lamp affects all observed paper properties. For all analyzed office papers, the values of the tensile index, Bekk smoothness, and pH of paper extracts decreased, while the values of elongation break, tear index, and Bendtsen roughness increased due accelerated aging. Regarding the CIE L*a*b* color space value, lightness (L*) generally decreased after the aging treatment, and all paper samples became less reddish (a* decreased) and more yellow (b* increased). The obtained results of this research reveal that pulp with hemp fibers can produce higher-quality office paper that is more stable against light and temperature influences than those made with post-consumer fibers. However, to increase the durability of manufactured paper, hemp fibers must be bleached.

Izvorni jezik
Engleski

Znanstvena područja
Grafička tehnologija, Kemijsko inženjerstvo

POVEZANOST RADA