Naslov
Increased reliability of modified polyolefin backsheet over commonly used polyester backsheets for crystalline PV modules

Autori
Omazic, Antonia ; Oreski, Gernot ; Edler, Michael ; Eder, Gabriele Christine ; Christina, Hirschl ; Pinter, Gerald ; Erceg, Matko

Izvornik
Journal of applied polymer science (0021-8995) Early view (2020); 1-8

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
Ageing ; Degradation ; Mechanical properties ; Thermal properties

Sažetak
The weathering stability of polymeric backsheets is very important for the reliability of photovoltaic (PV) modules. In addition to reliability, cost reduction and sustainability are upcoming challenges the PV backsheet industry is facing with. The most commonly used material for PV backsheets is poly(ethylene-terephthalate)-PET. However, PET is in general very sensitive to hydrolysis, which leads to chain scission and causes embrittlement, cracking, delamination, and dimensional instability of the backsheet. Compared to that newly developed modified polyolefin backsheets have favorable selective permeation properties and high mechanical flexibility, which could be key properties for backsheets in terms of higher PV module reliability. In this work, the weathering stability of PET/fluoropolymer backsheet and an alternative coextruded polyolefin-backsheet was investigated in terms of thermal and mechanical stability. Both materials were artificially aged and the changes caused by aging were investigated. The polyester-based backsheet showed embrittlement and reduced elongation at break for 70%. The polyolefin-based backsheet retained its mechanical flexibility even after 2000 h of aging under damp-heat conditions, with no significant physical or chemical aging processes occurring. The comparison of the results of both backsheets suggests that the polyolefin backsheet is a promising candidate for the reduction of cracks and delamination in the field

Izvorni jezik
Engleski

Znanstvena područja
Kemijsko inženjerstvo

POVEZANOST RADA