Inhibition of aluminium alloy corrosion in chloride solution by caffeine isolated from black tea

Autori
Gudić, Senka ; Zlatunić, Marija ; Vrsalović, Ladislav ; Radonić, Ani

Izvornik
Hrana u zdravlju i bolesti (2233-1220) 7 (2018), 1; 6-11

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
aluminium alloy ; corrosion ; inhibition ; caffeine

Sažetak
Caffeine (1, 3, 7-trimethylxanthine) was isolated from black tea and characterised using different physical methods. The corrosion inhibition performance of the caffeine isolate (in concentration from 110 -5 to 110 -3 mol/dm 3 ) on aluminium alloy corrosion in neutral 0.5 mol/dm 3 NaCl solution was investigated using potentiodynamic and linear polarization measurements at 20 C. Corrosion potential, corrosion current and polarization resistance were determined and surface coverage of inhibitor molecules and inhibition efficiency were calculated. The obtained results show that caffeine effectively inhibited the corrosion reaction in the chloride solution with an inhibition efficiency of up to  76%. Furthermore, caffeine was found to function essentially as a mixed type with a higher influence on cathodic reaction. The adsorption behaviour of investigated inhibitor can be described by the Freundlich adsorption isotherm. The adsorption free energy closes to -10 kJ/mol indicates physical adsorption of the caffeine on the aluminium alloy surface in NaCl solution.

Izvorni jezik
Engleski

Znanstvena područja
Kemija, Kemijsko inženjerstvo

Napomena
Glavni autor: Senka Gudić

POVEZANOST RADA