Naslov
Environment of the Eu3+ Ion within Nanocrystalline Eu-Doped BaAl2O4: Correlation of X-ray Diffraction, Mössbauer Spectroscopy, X-ray Absorption Spectroscopy, and Photoluminescence Investigations

Autori
Gržeta, Biserka ; Lützenkirchen-Hecht, Dirk ; Vrankić, Martina ; Bosnar, Sanja ; Šarić, Ankica ; Takahashi, Masashi ; Petrov, Dimitar ; Bišćan, Marijan

Izvornik
Inorganic chemistry (0020-1669) 57 (2018), 4; 1744-1756

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
Barium aluminate ; Europium doping ; Hydrothermal processing ; X-ray diffraction ; Mössbauer spectroscopy ; X-ray absorption spectroscopy ; Photoluminescence ; Crystal structure ; Microstructure

Sažetak
Powder samples of pure BaAl2O4 and doped with 4.9 atom % Eu in relation to Ba were prepared by a hydrothermal route. The samples were characterized by X-ray diffraction, 151Eu Mössbauer spectroscopy, synchrotron-based X-ray absorption spectroscopy at the Ba L3- and Eu L3- edges, and photoluminescence measurements. Diffraction lines were broadened, indicating that the samples were nanocrystallline.The samples possessed a hexagonal crystal structure, space group P63. 151Eu Mössbauer spectroscopy revealed the presence of Eu in the 3+ oxidation state. The same information on the Eu oxidation state was also obtained by the Eu L3-edge X-ray absorption near-edge structure of the doped sample. Extended X-ray absorption fine structure showed an Eu3+ ion substituted for Ba2+ on the Ba2 site in the BaAl2O4 host structure, with charge compensation by an interstitial O in the vicinity of the Ba2 site. That was confirmed by a Rietveld structure refinement for the Eu-doped BaAl2O4 sample. Analysis of the diffraction line broadening for the prepared samples was performed simultaneously with the structure refinement. Both the dopant Eu3+ and the interstitial O acted as defects in the host BaAl2O4 lattice, which increased the lattice strain from 0.02% for pure BaAl2O4 to 0.17% for the Eu-doped sample. Crystallite sizes in the samples increased with Eu doping from 32 nm for pure BaAl2O4 to 36 nm for Eu-doped BaAl2O4. This could likely be related to the increase in the diffusion rate of the cations in the sample when a part of the Ba2+ cation content was exchanged with smaller Eu3+ cations. The Eu- doped BaAl2O4 sample exhibited red photoluminescence under excitation with λexc = 308 nm. The observed emission spectrum indicated that Eu3+ ions occupied the Ba site with lower symmetry in the doped sample.

Izvorni jezik
Engleski

Znanstvena područja
Fizika, Kemija