Naslov
Isothermal and non-isothermal crystallization kinetics of zinc-aluminosilicate glasses

Autori
Tkalčec, Emilija ; Kurajica, Stanislav ; Ivanković, Hrvoje

Izvornik
Thermochimica Acta (0040-6031) 378 (2001), 1-2; 135-144

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
Crystallization kinetics ; Differential thermal analysis ; Gahnite ; Glass-ceramics ; Overlapping

Sažetak
Isothermal and non-isothermal differential thermal analysis (DTA), and X-ray diffraction (XRD) were used to study the nucleation and crystallization behavior of multicomponent Li2O-ZnO-Al2O3-B2O3-SiO2 glasses with ZrO2 and TiO2 as nucleating agents. The temperature of maximum nucleation rate for investigated glasses was found to be 1028 K. The crystallization of two phases (mullite s.s. and gahnite) occurs in a narrow temperature and time interval, respectively, therefore, the DTA curves are characterized by the superposition of exothermic peaks. Recently derived mathematical models have been applied for resolving the overlapping. The models enabled establishing the kinetic parameters for crystal growth of individual phases (mullite s.s. and gahnite). The activation energies for crystal growth were found to be in the range of 459-471 kJmol-1 and 368-386 kJmol-1 for mullite and gahnite, respectively. Avrami exponent n reveals three-dimensional growth of both phases.

Izvorni jezik
Engleski

Znanstvena područja
Kemijsko inženjerstvo

POVEZANOST RADA