Ion elution of laser-welded Co-Cr denture base metal alloys
Ion elution of laser-welded Co-Cr denture base metal alloys // IADR/PER Congress : abstracts ; u: Journal of Dental Research 93(S.I. C)
Dubrovnik, Hrvatska, 2014. (poster, međunarodna recenzija, sažetak, znanstveni)
CROSBI ID: 731689 Za ispravke kontaktirajte CROSBI podršku putem web obrasca
Naslov
Ion elution of laser-welded Co-Cr denture base metal alloys
Autori
Jelinić Carek, Andreja ; Živko Babić, Jasenka ; Jakovac, Marko ; Badel, Tomislav ; Crnojević, Helena ; Bago, Ivona
Vrsta, podvrsta i kategorija rada
Sažeci sa skupova, sažetak, znanstveni
Izvornik
IADR/PER Congress : abstracts ; u: Journal of Dental Research 93(S.I. C)
/ - , 2014
Skup
IADR/PER Congress Dubrovnik, 2014
Mjesto i datum
Dubrovnik, Hrvatska, 10.09.2014. - 13.09.2014
Vrsta sudjelovanja
Poster
Vrsta recenzije
Međunarodna recenzija
Ključne riječi
Alloys; Biocompatibility; Corrosion; Lasers and Metals
Sažetak
Objective: The goal of this study was to determine the concentration of Co, Cr and Ni eluted ions from laser welds of partial denture Co-Cr alloys. Method: Preparation of three Co- Cr dental alloys (Wisil M-Austenal, Köln, Germany ; I-MG-Interdent, Celje, Slovenia ; Brealloy F-400- Bredent, Senden, Germany) was performed according to ISO 6871-1 for static immersion test. The specimens were divided into two groups. The first group of samples was welded with Nd:YAG laser (Hercules ; Interdent, Celje, Slovenia) and second, unwelded, was used as a control group. The surfaces of the patterns were measured with accuracy of 0.1 cm2. The samples were exposed to the aqueous solution (0, 1mol/l lactic acid and 0, 1 mol/l sodium chloride) for 7 days at 37±1 °C. Ions elution was electrochemical tested by atomic absorption spectroscopy. Microstructure was analyzed before and after immersion test. After immersion, the samples surfaces were analyzed by scanning electron microscope TESCAN, Vega TS5136LS (Tescan, Brno, Czech Republic) with EDS system. Result: Elution of Co and Cr ions was statistically greater from laser welds. Nickel ions were found in both solutions, despite no declaration in analyzed alloys composition. Microstructure and SEM showed no differences before and after immersion test. In laser welds the cracks were visible. EDS analyses proved ions of Co, Cr, S, Hg and Si in laser welds, and Co, Cr, Mn, Mo, Si and C in control specimens. Conclusion : Laser welds proved less corrosion resistance because of cracks obtained during welding. The results suggest the control of working parameters during the welding.
Izvorni jezik
Engleski
Znanstvena područja
Dentalna medicina
POVEZANOST RADA
Projekti:
065-0650448-0439 - ISTRAŽIVANJE TERAPIJSKE UČINKOVITOSTI PROTETIČKIH GRADIVNIH MATERIJALA (Živko-Babić, Jasenka, MZOS ) ( CroRIS)
Ustanove:
Stomatološki fakultet, Zagreb
Profili:
Tomislav Badel
(autor)
Andreja Carek
(autor)
Jasenka Živko-Babić
(autor)
Ivona Bago
(autor)
Marko Jakovac
(autor)
Citiraj ovu publikaciju:
Časopis indeksira:
- Current Contents Connect (CCC)
- Web of Science Core Collection (WoSCC)
- Science Citation Index Expanded (SCI-EXP)
- SCI-EXP, SSCI i/ili A&HCI
- Scopus
- MEDLINE