Visible light activated photo-catalytic effect and local structure of iron silicate glass prepared by sol-gel method

Autori
Kubuki, S. ; Takahashi, Y. ; Akiyama, K. ; Homonnay, Z. ; Kuzmann, E. ; Sinko, K. ; Ristić, Mira ; Nishida, T.

Vrsta, podvrsta i kategorija rada
Sažeci sa skupova, sažetak, znanstveni

Izvornik
Book of abstracts of the International Conference on the Applications of the Mossbauer Effect - ICAME 2013 / Musić, Svetozar ; Ristić, Mira ; Krehula, Stjepko ; Petrović, Željka - Zagreb : Institut Ruđer Bošković, 2013, 295-295

ISBN
978-953-6690-97-8

Skup
International Conference on the Applications of the Mossbauer Effect - ICAME 2013

Mjesto i datum
Opatija, Hrvatska, 01.09.2013. - 06.09.2013

Vrsta sudjelovanja
Poster

Vrsta recenzije
Međunarodna recenzija

Ključne riječi
Iron silicate glass; Sol-gel method; α-Fe2O3; Photo-catalytic effect; UV-ViS; Mossbauer spectroscopy

Sažetak
Anatase type TiO is well known as a photo- catalyst activated by the UV light. It will be more effective to develop photo-catalyst which shows photo catalysis under visible light irradiation. Recently, Kubuki et al. revealed that 15Na2O•15CaO•xFe2O3•(70–x)SiO with ‘x’ between 10 and 50 mass% exhibited chemical oxygen demand (COD) decomposing ability. This result implies that iron silicate glass might be utilized as a purifier of polluted water. In this study, we report a relationship between local structure and visible light activated photo-catalytic effect of xFe2O3·(100–x)SiO2 glass prepared by sol-gel method. method. Iron silicate glass with a composition of xFe2O3·(100–x)SiO (in mass %, x = 10-50) were prepared by a sol-gel method. Reagent chemicals of Si(OC2H5)4, Fe(NO3)3·9H2O, 7.8 M HNO3, and C2H5OH were poured into a beaker and well mixed for 2 h at RT. After having been agitated by refluxheat method at 80ºC for 2h, the solution was poured into a glass vial and dried at 60ºC for 3 days to prepare gel samples of dark brown color. It was annealed at 1000ºC for 3 h in air. For evaluation of photo-catalytic effect, 40mg of well-pulverized annealed samples were soaked into 20 ml of methylene blue aqueous solution (MBaq) with a concentration of 20µΜ. Irradiation test was carried out for 2 h at RT in a darkroom using a glass vial irradiated with a visible light having the wavelength range of 420-750 nm. Absorbance (Abs.) of MBag before and after the irradiation test was determined by UV-VIS. 57^Fe-Mössbauer spectra were measured by a constant acceleration mode with a source of Co(Rh) and a reference of α-Fe. Absorption area (A) for the magnetic sextet with isomer shift and internal magnetic field (Hint) of 0.37 mm s^-1 and 51.4 T increased from 0.0 to 10.3 and 100 % with Fe2O3 content (x), indicating an increase in the fraction of hematite (α-Fe2O3). Decrease in the Abs. of MB became larger after 2h-irradiation test with an increase of ‘x’. It is concluded that MB-decomposing ability is associated with the amount of α-Fe phase precipitated in the annealed iron silicate glass.