Effect of compaction pressure on the densification of cold isostatically pressed alumina ceramics
Effect of compaction pressure on the densification of cold isostatically pressed alumina ceramics // CIM 2013 : Computer integrated manufacturing and high speed machining / Abele, Eberhard ; Udiljak, Toma ; Ciglar, Damir (ur.).
Zagreb: Hrvatska udruga proizvodnog strojarstva (HUPS), 2013. str. 105-108 (predavanje, međunarodna recenzija, cjeloviti rad (in extenso), znanstveni)
CROSBI ID: 637310 Za ispravke kontaktirajte CROSBI podršku putem web obrasca
Naslov
Effect of compaction pressure on the densification of cold isostatically pressed alumina ceramics
Autori
Ćurković, Lidija ; Majić Renjo, Marijana ; Ciglar, Damir
Vrsta, podvrsta i kategorija rada
Radovi u zbornicima skupova, cjeloviti rad (in extenso), znanstveni
Izvornik
CIM 2013 : Computer integrated manufacturing and high speed machining
/ Abele, Eberhard ; Udiljak, Toma ; Ciglar, Damir - Zagreb : Hrvatska udruga proizvodnog strojarstva (HUPS), 2013, 105-108
ISBN
978-953-7689-02-5
Skup
14th International Scientific Conference on Production Engineering
Mjesto i datum
Biograd na Moru, Hrvatska, 19.06.2013. - 22.06.2013
Vrsta sudjelovanja
Predavanje
Vrsta recenzije
Međunarodna recenzija
Ključne riječi
Al2O3 ceramics; CIP; densification
Sažetak
Ceramic parts are generally produced by combination of compaction and sintering. In this paper, cold isostatic pressing (CIP) for compaction and shaping of alumina ceramics was used. This method provides green compacts of uniformly distributed high density with the absence of large pores. Prepared green bodies were sintered at the temperature of 1650°C. Influence of different particle size distribution of alumina powders and compaction pressure on green and sintered density was investigated. It was found that green, as well as sintered density slightly increased with increasing compaction pressure and decreasing alumina particle size powders. The linear shrinkage of ceramic samples during sintering was 20 to 22 %.
Izvorni jezik
Engleski
Znanstvena područja
Strojarstvo
POVEZANOST RADA
Projekti:
120-1201833-1789 - Istraživanje strukture i svojstava tehničke keramike i keramičkih prevlaka (Ćurković, Lidija, MZOS ) ( CroRIS)
120-1521473-1808 - Povišenje učinkovitosti razvoja i preradbe polimernih proizvoda (Šercer, Mladen, MZOS ) ( CroRIS)
120-1201948-1938 - Napredni obradni sustavi i procesi (Udiljak, Toma, MZOS ) ( CroRIS)
Ustanove:
Fakultet strojarstva i brodogradnje, Zagreb