Naslov
Probing the mesh formed by the semirigid polyelectrolytes

Autori
Salamon, Krešimir ; Aumiler, Damir ; Pabst, Georg ; Vuletić, Tomislav

Izvornik
Macromolecules (0024-9297) 46 (2013), 3; 1107-1118

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
polyelectrolytes; SAXS; FCS; impedance spectroscopy; DNA; hyaluronic acid

Sažetak
We correlate conformation and dynamics of the semirigid polyelectrolytes deoxyribonucleic acid (DNA) and hyaluronic acid (HA) in the semidilute regime, across a broad concentration range (10^−3 − 10^2 g/L). Salt-free polyelectrolytes are distinct from uncharged polymers as they presumably form a rather rigid, isotropic mesh. The polyelectrolyte characteristic mesh size is known as de Gennes correlation length ξ. We directly probed the mesh formed by DNA and HA, by employing fluorescence correlation spectroscopy (FCS) to measure the diffusion coefficient of fluorescently labeled DNA fragments added in trace amounts. For the salt-free solutions we found that the DNA or HA mesh size has to be 2−3 times larger than the fragments for them to start to diffuse freely (as if in the dilute solution). For a tighter mesh (concentrations 0.1−1 g/L), the fragment diffusion coefficient is only half the free diffusion value. Conversely, fragments show the free diffusion coefficient as if there is no meshin DNA or HA in 10 mM buffer. This complies well with the fact that the ξ fades for polyelectrolytes with added salt. The diffusion coefficient falls off further when the mesh size gets smaller than the fragment size (above 1 g/L) and a similar value is reached in buffer as well as in pure water, respectively, at the highest measured concentrations (10 g/L). We also performed small-angle X-ray scattering (SAXS) on HA and DNA (range 3−130 g/L) to complement our previous dielectric spectroscopy (DS) studies (range 0.01−5 g/L). Combined, these methods provide reference values of the de Gennes length ξ across the range studied by FCS.

Izvorni jezik
Engleski

Znanstvena područja
Fizika

POVEZANOST RADA