Pregled bibliografske jedinice broj: 626077
Hydration of B2O3-stabilized α′- and β-modifications of dicalcium silicate
Hydration of B2O3-stabilized α′- and β-modifications of dicalcium silicate // Cement and concrete research : including advanced cement based materials, 8 (1978), 2; 173-180 doi:10.1016/0008-8846(78)90006-6 (međunarodna recenzija, članak, znanstveni)
CROSBI ID: 626077 Za ispravke kontaktirajte CROSBI podršku putem web obrasca
Naslov
Hydration of B2O3-stabilized α′- and β-modifications of dicalcium silicate
Autori
Jelenić, Ivanka ; Bezjak, Aleksandar ; Bujan, Marija
Izvornik
Cement and concrete research : including advanced cement based materials (0008-8846) 8
(1978), 2;
173-180
Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni
Ključne riječi
cement ; hydration ; dicalcium silicate
Sažetak
Paste hydration of B2O3-stabilized α′- and β-C2S was studied at reaction times between 5 hours and 28 days. Data on the degree of hydration determined by X-ray diffraction at different ages were used to evaluate hydration rate constants. The higher rate of α′- C2S hydration resulted in the higher compressive strengths of the α′-C2S-alite paste as compared with the β-C2S-alite paste. Differences in crystal imperfections of the two C2S-polymorphs were determined using electron microscopy and electron diffraction
Izvorni jezik
Engleski
Znanstvena područja
Kemija
POVEZANOST RADA
Ustanove:
Farmaceutsko-biokemijski fakultet, Zagreb
Citiraj ovu publikaciju:
Časopis indeksira:
- Web of Science Core Collection (WoSCC)
- Science Citation Index Expanded (SCI-EXP)
- SCI-EXP, SSCI i/ili A&HCI
- Scopus