Gas barrier and morphology characteristics of linear low-density polyethylene and two different polypropylene films

Autori
Kurek, Mia ; Klepac, Damir ; Ščetar, Mario ; Galić, Kata ; Valić, Srećko ; Liu, Yong ; Yang, Weimin

Izvornik
Polymer bulletin (0170-0839) 67 (2011), 7; 1293-1309

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
activation energy; polyolefins; differential scanning calorimetry (DSC); gas permeation

Sažetak
In this research, linear low-density polyethylene (PE-LLD), cast polypropylene (PPcast), and bioriented coextruded polypropylene (BOPP) were used as polymeric materials. Permeability, diffusivity, and solubility of N2, O2, and CO2 through above polymers were obtained at different temperatures. The structure and thermal–mechanical features of the films were characterized by scanning electron microscopy (SEM) and differential scanning calorimetry (DSC). The permeability, diffusivity, solubility, and their temperature dependency were studied by correlations with gas molecule properties. The highest permeation coefficients (>3.8 × 10−8 cm3 cm−1 s−1 bar−1) are obtained for PPcast at 60 °C. Activation energy for permeation follows the sequence: N2 > O2 > CO2 for PE-LLD and PPcast. On the other hand, the diffusion activation energy follows the order: O2 > CO2 > N2 and N2 > CO2 > O2 for PE-LLD and PPcast, respectively. In the case of BOPP, activation energy follows the sequence: O2 > CO2 > N2 ; CO2 > N2 > O2 ; and O2 > CO2 > N2 for permeation, diffusion, and heat of sorption, respectively.

Izvorni jezik
Engleski

Znanstvena područja
Kemija, Prehrambena tehnologija

POVEZANOST RADA