Thermal evolution of calcium aluminate gel obtained from aluminium sec-butoxide chelated with ethyl acetoacetate

Autori
Kurajica, Stanislav ; Mandić, Vilko ; Šipušić, Juraj

Izvornik
Journal of Ceramic Science and Technology (2190-9385) 2 (2011), 1; 15-22

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
calcium aluminate ; sol-gel ; thermal evolution ; crystallization ; non-isothermal kinetics

Sažetak
Calcium aluminate (CaAl2O4) powder was prepared with a sol-gel technique using calcium nitrate tetrahydrate and aluminium sec-butoxide as precursors and ethyl acetoacetate as chelating agent. The dried gel and thermally treated samples were characterized by means of simultaneous Differential Thermal and Thermo-Gravimetric Analysis (DTA/TGA), Fourier Transform Infrared spectroscopy (FTIR), and X-Ray Diffraction (XRD). From the results obtained, the thermal evolution of the prepared gel, the crystallization behaviour and crystallization kinetics are discussed. It has been established that the decomposition of the chelate and the evaporation of ethyl acetoacetate followed by an auto-combustion process occur in a lower temperature range. The crystallization process starts at temperatures higher than 900 °C. Calcium aluminate, CaAl2O4, appears as the major crystalline phase, and calcium dialuminate, CaAl4O7, and dodecacalcium heptaaluminate, Ca12Al14O33, as minor phases. The crystallization processes of the phases proceed simultaneously and independently. Thermal treatment at higher temperature increases the amount of calcium aluminate and decreases the amount of minor components.

Izvorni jezik
Engleski

Znanstvena područja
Kemijsko inženjerstvo

POVEZANOST RADA