The effect of solution heat treatment on microstructure, fracture resistance and hardness of AISI 310S steel

Autori
Gojić, Mirko ; Kožuh, Stjepan ; Kosec, Ladislav ; Holjevac-Grgurić, Tamara

Vrsta, podvrsta i kategorija rada
Radovi u zbornicima skupova, cjeloviti rad (in extenso), znanstveni

Izvornik
MATRIB 2010 / Schauperl, Zdravko ; Šnajdar, Mateja - Zagreb : Hrvatsko društvo za materijale i tribologiju (HDMT), 2010, 123-129

ISBN
978-953-7040-18-5

Skup
15th International conference on materials, tribology, recycling

Mjesto i datum
Vela Luka, Hrvatska, 23.06.2010. - 25.06.2010

Vrsta sudjelovanja
Predavanje

Vrsta recenzije
Međunarodna recenzija

Ključne riječi
heat resistant steel ; microstructure ; hardness ; fractography

Sažetak
In present work, the hardness, fracture mode and microstructure of heat resistant stainless steel AISI 310S before and after solution heat treatment were investigated. Temperature of solution heat treatment was 1100°C/30 minutes and after solution heat treatment the samples were quenched in water (15°C). Microstructure and fracture surface analysis were carried out with scanning electron microsope (SEM) and energy dispersive X-ray spectrometer (EDX). Microstructure of steel before heat treatment consisted of austenite and delta ferrite. Also, microstructure of steel after solution heat treatment and quenching was heterogeneous and consisted of austenite and delta ferrite. Sigma phase particles were not observed. Solution heat treatment a slight influence on the hardness decreasing (from 203 to 170 HV). Fracture surface before and after solution heat treatment characterized by a ductile fracture mode.