Utjecaj etilen/propilen/dienskog kaučuka kao kompatibilizatora na mehanička svojstva i morfologiju mješavine polipropilena i polietilena niske gustoće
Utjecaj etilen/propilen/dienskog kaučuka kao kompatibilizatora na mehanička svojstva i morfologiju mješavine polipropilena i polietilena niske gustoće // Polimerni materijali i dodatci polimerima / Čatić, Igor (ur.).
Zagreb: Društvo za plastiku i gumu, 2009. str. 96-102 (predavanje, domaća recenzija, cjeloviti rad (in extenso), znanstveni)
CROSBI ID: 435002 Za ispravke kontaktirajte CROSBI podršku putem web obrasca
Naslov
Utjecaj etilen/propilen/dienskog kaučuka kao kompatibilizatora na mehanička svojstva i morfologiju mješavine polipropilena i polietilena niske gustoće
(Influence of ethylene/propylene/diene rubber as compatibilizer on mechanical properties and morphology of polypropylene and low density polyethylene blend)
Autori
Vranješ, Nina ; Rek, Vesna ; Fiamengo, Ivona
Vrsta, podvrsta i kategorija rada
Radovi u zbornicima skupova, cjeloviti rad (in extenso), znanstveni
Izvornik
Polimerni materijali i dodatci polimerima
/ Čatić, Igor - Zagreb : Društvo za plastiku i gumu, 2009, 96-102
Skup
Savjetovanje Polimerni materijali i dodatci polimerima
Mjesto i datum
Zagreb, Hrvatska, 19.11.2009. - 20.11.2009
Vrsta sudjelovanja
Predavanje
Vrsta recenzije
Domaća recenzija
Ključne riječi
mješavine polipropilena i polietilena niske gustoće ; kompatibilizacija ; morfologija ; mehanička
(blends of polypropylene and low density polyethylene ; compatibilization ; morphology ; mechanical)
Sažetak
Polypropylene (PP) and polyethylene (PE)represent a major part of plastic waste. Therefore, the research was focused on the characterization of a mixture of PP and PE-LD. Since most of the polymers are immiscible and incompatible, improvement of the compatibility of PP/PE-LD blends has been achieved in the addition of ethylene/propylene/diene rubber (EPDM) as compatibilizer. Tensile strength at break, elongation at break and Izod impact strength have been chosen to evaluate the effectiveness of EPDM in these blends. Glass transition temperature and the stiffness of PP/PE-LD blends with and without EPDM were determinate by dynamic-mechanical analysis (DMA). Blend morphology was explored using scanning electronic microscope. Addition of EPDM reduced the tensile strength at break and improved elongation at break. Blends of PP/PE-LD/EPDM showed higher values of Izod impact strength. Storage modulus of PP was reduced by EPDM addition. SEM micrographs of PP/PE-LD/EPDM blends showed better compatibility.
Izvorni jezik
Hrvatski
Znanstvena područja
Kemijsko inženjerstvo
POVEZANOST RADA
Projekti:
MZOS-125-1252971-2578 - Modifikacija i stabilnost višefaznih polimernih sustava (Govorčin-Bajsić, Emi, MZOS ) ( CroRIS)
Ustanove:
Fakultet kemijskog inženjerstva i tehnologije, Zagreb