SOL-GEL SYNTHESIS AND CHARACTERIZATION OF Nb2O5 POWDERS

Autori
Ristić, Mira ; Popović, Stanko ; Musić, Svetozar

Vrsta, podvrsta i kategorija rada
Sažeci sa skupova, sažetak, znanstveni

Izvornik
Book of abstracts of the 13th Slovenian-Croatian Crystallographic Meeting / Leban, Ivan - Ljubljana, 2004

Skup
13th Slovenian-Croatian Crystallographic Meeting

Mjesto i datum
Bovec, Slovenija, 17.06.2004. - 20.06.2004

Vrsta sudjelovanja
Predavanje

Vrsta recenzije
Nije recenziran

Ključne riječi
Nb2O5; sol-gel; DTA; FT-IR; XRD; FE SEM

Sažetak
Niobium(V)-oxide (Nb2O5) has found important applications in the production of ferroelectric and electrochromic devices. The properties of Nb2O5 strongly depend on its synthesis procedure and the conditions of thermal treatment. For that reason many researchers have been trying to change the properties of Nb2O5 by changing the synthesis procedures. Nb2O5 powders were prepared by the sol-gel procedure. Nb(OC2H5)5 dissolved in ethanol was (a) rapidly hydrolysed by adding a concentrated NH4OH solution, or (b) slowly hydrolysed by adding a small amount of H2O. The Nb2O5 powders were characterized by XRD, DTA / TGA, FT-IR spectroscopy and SEM. The initial Nb2O5 powders were amorphous. Upon heating at 300 oC of the amorphous powder obtained by the method (a) there was no change as shown by XRD, whereas the amorphous powder obtained by the method (b) and also heated at 300 oC contained Nb2O5 (TT phase) plus an amorphous fraction. The amorphous powders heated at 500 oC contained Nb2O5 (TT-phase), whereas at 650 oC the Nb2O5 (T-phase) was obtained. Crystallite sizes were determined using the Scherrer method. The agreggates of nanosized Nb2O5 were present in amorphous Nb2O5 precursors and upon their heating at 300 oC, whereas upon heating at 650 oC a porous interconnected microstructure was formed in both preparations, (a) and (b), as shown by SEM.