Naslov
Factors that may influence the micro-emulsion synthesis of nanosize magnetite particles

Autori
Gotić, Marijan ; Jurkin, Tanja ; Musić, Svetozar

Izvornik
Colloid and Polymer Science (0303-402X) 285 (2007), 7; 793-800

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
micro-emulsion; gamma-irradiation; goethite; magnetite; Si-ferrihydrite

Sažetak
The influence of experimental conditions on the formation of nanosize magnetite by micro-emulsion method was investigated using Mossbauer and FT-IR spectroscopies, FE SEM/EDS and TEM. It was found that the concentration of starting chemicals (FeCl3/FeSO4, aeration/de-aeration, high alkalinity and gamma-irradiation influenced this precipitation process. Rod-like goethite particles 200-300 nm long and up to 10 nm wide were obtained by destabilization of the micro-emulsion aged 5 to 45 days at RT. Si-containing ferrihydrite was also formed and it retarded the formation of goethite by the dissolution/re-precipitation mechanism. A small amount of Si from a glass flask was dissolved. A very strong influence of gamma-irradiation of the formation of nanosize magnetite by micro-emulsion method was observed. Gamma-irradiation created strong reductive conditions in the micro-emulsion. At an around 460 kGy dose, nanosize magnetite particles sized around 5 to 20 nm and very small amount of goethite particles were obtained. The EDS measurements on the particles suggested the formation of sub-stoichiometric magnetite (Fe3-xO4)and not maghemite. This finding is in line with the strong reductive conditions induced with gamma-irradiation.

Izvorni jezik
Engleski

Znanstvena područja
Kemija

POVEZANOST RADA