Structural Changes of Sol-gel Derived Sn-doped In_2O_3 due to Annealing at 1000 ºC

Autori
Gržeta, Biserka ; Tkalčec, Emilija ; Goebbert, Christian ; Popović, Jasminka ; Ksenofontov, Vadim ; Reiman, Sergey ; Felser, Claudia

Vrsta, podvrsta i kategorija rada
Sažeci sa skupova, sažetak, znanstveni

Izvornik
Abstracts of the XX Congress of the International Union of Crystallography ; u: Acta Crystallographica A 61(2005) Part 1 / Maelli, Carlo ; Paoli, Paola - Firenza : München : International Union of Crystallography, 2005, C395-C395

Skup
Congress of the International Union of Crystallography (10 ; 2005)

Mjesto i datum
Firenca, Italija, 23.08.2005. - 31.08.2005

Vrsta sudjelovanja
Poster

Vrsta recenzije
Međunarodna recenzija

Ključne riječi
Sn-doped In_2O_3; X-ray diffraction; Moessbauer spectroscopy

Sažetak
Sn doped In_2O_3 (ITO) is an n-type, highly degenerate, wide-gap semiconductor. Its electrical and optical properties are associated with microstructure as well as with the preparation methods and conditions [1]. Although it is widely used in optoelectronic devices, its structure is not well understood yet. A set of ITO samples containing 0-14 at% Sn was prepared by a sol-gel technique from InCl_3 and SnCl_4 [2]. The samples were additionally annealed at 1000 º ; C for 1 h, slowly cooled to RT and examined by XRD and ^(119)Sn Moessbauer spectroscopy. XRD revealed that the samples were isostructural with In_2O_3 [3]. Lattice parameter a increased almost linearly with Sn-content from the value of 10.1215(5) angstrom for pure In_2O_3 to 10.1319(4) angstrom for 14 at% Sn. While ^(119)Sn Moessbauer spectra of the as-prepared samples are characterized with two doublets corresponding to two different cation sites (B and D, respectively), the spectra of annealed samples contained extremely broad subspectrum in addition. Decrease of temperature from 300K to 10K caused disappearance of the broad component. This unusual broad Moessbauer subspectrum could be explained by a diffusional motion of Sn^4+ ions.