Gradual recrystallisation of metamict fergusonite: X-ray diffraction and Raman spectroscopy study

Autori
Tomašić, Nenad ; Gajović, Andrea ; Bermanec, Vladimir

Vrsta, podvrsta i kategorija rada
Sažeci sa skupova, sažetak, znanstveni

Izvornik
Mitteilungen der Österreichischen Mineralogischen Gesellschaft / Koller, Friedrich et al. - Beč : Österreichische Mineralogische Gesellschaft, 2004, 98-98

Skup
6th EMU School "Spectroscopic Methods in Mineralogy" & ECMS 2004, 5th European Conference on Mineralogy and Spectroscopy

Mjesto i datum
Beč, Austrija, 30.08.2004. - 08.09.2004

Vrsta sudjelovanja
Poster

Vrsta recenzije
Međunarodna recenzija

Ključne riječi
fergusonite; metamictisation; recrystallisation; XRD; Raman spectroscopy
(ergusonite; metamictisation; recrystallisation; XRD; Raman spectroscopy)

Sažetak
GRADUAL RECRYSTALLISATION OF METAMICT FERGUSONITE: X-RAY DIFFRACTION AND RAMAN SPECTROSCOPY STUDY Tomašić, N. 1, Gajović, A.2 & Bermanec, V.1 1 University of Zagreb, Institute of Mineralogy and Petrography, Horvatovac bb, HR-10000 Zagreb, Croatia 2 Ruđer Bošković Institute, POB 180, 10002 Zagreb, Croatia e-mail:.ntomasic@jagor.srce.hr Fergusonite mineral samples, mainly represented as YNbO4, are frequently metamict. Heating experiments induce crystal structure recovery, but also cause phase transition processes, since fergusonite is a polymorphic substance (Wolten & Chase, 1967). X-ray powder diffraction and Raman spectroscopy were employed to monitor the sequences of fergusonite recrystallisation. The corresponding Raman spectra were also used to reveal possible presence of original structure remnants in the metamict mineral. Two metamict mineral samples previously identified as fergusonite were heated in air at 400, 500, 650, 800, 1000 and 1300°C for 24 hours in each case. The mineral sample from Bakkane-Steane, Norway, was completely amorphous to X-rays and started to recrystallise at 400°C with scheelite type structure (space group I41/a) being stable up to 1000°C. At 1000°C monoclinic (space group I2)  -fergusonite dominated, with the tetragonal phase still present. At 1300°C the transformation from tetragonal to monoclinic fergusonite was completed. Raman spectra confirmed the gradual fergusonite recrystallisation by sharpening and intensifying of vibrational bands. The number of bands increased with the lowering of the symmetry. For the metamict mineral the vibrational bands at 779, 685, 697, 310, 208 and 108 cm-1 were present indicating the residue of the original crystal structure. At lower heating temperatures the bands were broad, but at higher temperatures reappeared more sharpened, resolved and intensified. The second mineral sample, originating from Ytterby, Sweden, was almost completely metamict, with only a few low intensity diffraction lines superimposed on the characteristic amorphous diffraction peak. At 400°C pyrochlore phase started to recrystallise being continuously present through the whole temperature range. At 1000°C the monoclic  -fergusonite appeared with recrystalisation completed at 1300°C. Raman bands were similar to those of fergusonite from Bakkane-Steanne, although some of them had different intensities and were slightly shifted. Vibration bands were not present in the spectrum of the unheated metamict mineral. The vibrational spectra of the complex oxide structures are difficult to calculate, but a relation to the analogous synthetic compounds (Yashima et al., 1997) could be established. McConnell et al. (1976) indicate that LO and TO Nb-O stretching modes of niobium oxides appear in range 1010-620 cm-1. Therefore, observed lattice vibrations reveal partial preservation of Nb-O polyhedra stacking in metamict fergusonite from Bakkane-Steane. References McCONNELL, A. A., ANDERSON, J. S. & RAO, C. N. R. (1976): Spectrochim. Acta, A 32: 1067-1076 WOLTEN, G. M & CHASE, A. B. (1967): Am. Miner., 52: 1536-1541. YASHIMA, M., LEE, J.H., KAKIHANA, M. & YOSHIMURA, M. (1997): J. Phys. Chem. Solids, 58(10): 1593-1597