Stainless Steel Crevice Corrosion Assessed in the Flowing System

Autori
O.Lahodny-Šarc, Lj.Krstulović, B.Kulušić, J.Ivić, D.Sambrailo

Vrsta, podvrsta i kategorija rada
Radovi u zbornicima skupova, cjeloviti rad (in extenso), znanstveni

Izvornik
Proceed. EUROCORR 2003, The European Corrosion Congress, European Federation of Corrosion, Event No. 261 / - Budimpešta, 2003, Paper no. 131, pp. 1-10

Skup
EUROCORR 2003, The European Corrosion Congress, European Federation of Corrosion, Event No. 261

Mjesto i datum
Budimpešta, Mađarska, 28.09.2003. - 02.10.2003

Vrsta sudjelovanja
Predavanje

Vrsta recenzije
Međunarodna recenzija

Ključne riječi
stainless steel; crevice corrosion; flowing system; seawater
(stainless steel; crevice corrosion flowing system; seawater)

Sažetak
The tendency of four types of stainless steel, austenitic UNS S31600, UNS S31254, and two duplex steels SAF 2205, UNS S32205, and SAF 2507, UNS S32750, toward initiation and propagation of crevice corrosion has been investigated in the flowing system of natural seawater in the Adriatic sea, at the location in Dubrovnik, Croatia.A new crevice corrosion testing method, developed by the Working Party on Marine Corrosion of the European Federation of Corrosion has been applied to assess crevice corrosion behaviour of stainless steel. Metal specimens mounted with crevice formers have been used for the monitoring the free corrosion potential in seawater during six months. At the same time the temperature, salinity, redox potential, the oxygen content changes, and the presence of bio film on the metal surace were detected.Particular attention has been payed to the mounting of plastic crevice formers in order to eliminate any corrosion process besides that one under the crevice formers, which were held with washers, bolts and nuts of titanium. Sharp drop of the corrosion potential was used as an indicator of crevice corrosion initiation.As expected, the initiation and propagation phenomena were found to differ due to the type of stainless steel. After exposure in the seawater crevice formers were removed for visual and microscopic inspection of the crevice area on the specimen, and the weight loss measuremen.