INFLUENCE OF SURFACE ROUGHNESS ON THE RATE OF CORROSION PENETRATION INTO THE STEEL
INFLUENCE OF SURFACE ROUGHNESS ON THE RATE OF CORROSION PENETRATION INTO THE STEEL // Metalurgija, 62 (2023), 1; 99-102 (međunarodna recenzija, članak, znanstveni)
CROSBI ID: 1211779 Za ispravke kontaktirajte CROSBI podršku putem web obrasca
Naslov
INFLUENCE OF SURFACE ROUGHNESS ON THE RATE OF
CORROSION PENETRATION INTO THE STEEL
Autori
Šolić, Tomislav ; Marić, Dejan ; Bašić, Aleksandar ; Samardžić, Ivan
Izvornik
Metalurgija (0543-5846) 62
(2023), 1;
99-102
Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni
Ključne riječi
steel ; corrosion ; rate of corrosion ; roughness ; weighing
Sažetak
This research analyses the influence of surface roughness on the rate of corrosion penetration into the steel. The test specimens were mechanically treated with fine abrasive jet to make their surface slightly rougher than it was in the initial state. The test specimens were then kept in conditions of atmospheric corrosion for 90 days to be tested afterwards by weighing, i.e. by the mass loss method. The analysis showed that a slight increase in surface roughness facilitated faster development of corrosion mechanisms, thus drastically increasing the rate of corrosion penetration into the material. Changes in surface roughness can be also caused by abrasion or erosion damage, so it is important to choose adequate surface protection technologies for prevention of unwanted wear of the steel.
Izvorni jezik
Engleski
Znanstvena područja
Strojarstvo
POVEZANOST RADA
Ustanove:
Strojarski fakultet, Slavonski Brod,
Sveučilište u Slavonskom Brodu
Citiraj ovu publikaciju:
Časopis indeksira:
- Web of Science Core Collection (WoSCC)
- Emerging Sources Citation Index (ESCI)
- Scopus