Naslov
Characterization of welded duplex stainless steel after annealing

Autori
Kožuh, Stjepan ; Kovačević, Domagoj ; Ivanić, Ivana ; Kosec, Borut ; Gojić, Mirko

Vrsta, podvrsta i kategorija rada
Radovi u zbornicima skupova, cjeloviti rad (in extenso), znanstveni

Izvornik
Proceedings Book of 19th International Foundrymen Conference / Dolić, Natalija, Zovko Brodarac, Zdenka, Brajčinović, Sandra - Sisak : Metalurški fakultet Sveučilišta u Zagrebu, 2021, 372-382

ISBN
978-953-7082-39-0

Skup
19th International Foundrymen Conference Humans – Valuable Resource for Foundry Industry Development

Mjesto i datum
Split, Hrvatska, 16.06.2021. - 18.06.2021

Vrsta sudjelovanja
Poster

Vrsta recenzije
Međunarodna recenzija

Ključne riječi
duplex stainless steel, microstructure, microhardness, welding, annealing

Sažetak
In this work microstructure analysis and microhardness testing was carried out on duplex stainless steel X2CrNiMoN22-5-3 after welding and annealing. Investigated stainless steel was welded using two welding procedures. The root of weld join was performed with TIG process and for filling SMAW process was used. Analysis of microstructure and microhardness was carried out before and after annealing. Annealing of welded joint was performed at temperature of 850 °C in duration for 60 minutes followed by cooling in air. After annealing, the samples were metallographic prepared. Optical microscopy and scanning electron microscopy with energy dispersive spectrometer were used for characterization of microstructure. Results shows that before annealing microstructure was consisted of ferrite and austenite, and after annealing presence of sigma phase was determined in weld metal. Microhardness values of samples before and after annealing was determined by Vickers method. A significant increase in microhardness values was observed in weld metal after annealing (from 294.9 HV1 to 357.0 HV1).