Naslov
Size-Reduction Induced Properties Modifications of Antiferromagnetic Dielectric Nanocrystalline Ba2NiMO6 (M = W, Te) Double Perovskites

Autori
Bijelić, Jelena ; Tatar, Dalibor ; Sahu, Manisha ; Jagličić, Zvonko ; Djerdj, Igor

Izvornik
Oxford Open Materials Science (2633-6979) 1 (2021), 1; Itaa003, 9

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
antiferromagnetic ; double perovskites ; high-κ dielectrics ; nanomaterials ; size-dependent

Sažetak
The main objective of this work was to synthesize phase pure double perovskites Ba2NiTeO6 (BNTO) and Ba2NiWO6 (BNWO) in nanocrystalline form and to reveal the impact of nanocrystallinity onto their magnetic and dielectric properties. The studied double perovskites were synthesized in nanocrystalline form by employing citrate sol-gel route. A detailed investigation of their structure and properties using X-ray powder diffraction (XRD), scanning electron microscopy (SEM), Raman spectroscopy technique, energy-dispersive X-ray spectroscopy (EDS), SQUID magnetometry and electrical measurements is carefully described. Rietveld refinement of XRD patterns revealed phase purity of both compounds, BNTO is trigonal (R-3m) while BNWO is cubic (Fm-3m). Raman spectroscopy studies reveal optical phonons that correspond to vibrations of Te6+/W6+O6 octahedra, while SEM images show irregular plate-like nanocrystals. Magnetic property measurements speak in favor of antiferromagnetic order but in both compounds size reduction affected their properties. BNTO has Néel temperature (TN) of 10.3 K which is higher than previously reported for its bulk form. Magnetic ground state of BNWO can be explained as canted antiferromagnetism with TN = 48.2 K. Room temperature measurements of dielectric constants at various frequencies suggest that these materials are high-κ dielectrics with low dielectric loss. The Nyquist plot reveals depressed semicircle arc typical for non-Debye type of relaxation phenomena for BNWO ceramic, whereas for BNTO ceramic almost straight line of Zʹʹ versus Z’ has been observed indicating its high insulating behavior. To conclude, size- dependent properties of studied double perovskites are discussed introducing a possibility for implementation in electronic devices.

Izvorni jezik
Engleski

Znanstvena područja
Fizika, Kemija

POVEZANOST RADA