CORROSION RESISTANCE OF THE X6CrNiTi18-10 MATERIAL EXPOSED TO A SALT SPRAY TEST (CROSBI ID 262815)
Prilog u časopisu | prethodno priopćenje | međunarodna recenzija
Podaci o odgovornosti
Šolić, Tomislav ; Marić, Dejan ; Putnik, Ivan ; Samardžić, Ivan
engleski
CORROSION RESISTANCE OF THE X6CrNiTi18-10 MATERIAL EXPOSED TO A SALT SPRAY TEST
The research was focused on testing the corrosion resistance of the X6CrNiTi18-10 material. This material exhibits good corrosion resistance in the humid atmosphere, but with the occurrence of chloride inclusion in the same atmosphere, its corrosion resistance is drastically reduced. The X6CrNiTi18-10 material is austenitic stainless steel susceptible to pitting corrosion and this can cause problems during exploitation of the construction made of this material. In order to determine the likelihood of pitting corrosion occurrence, a light microscopy was performed on testsamples that were exposed to the salt spray test chamber atmosphere, i.e. sprayed with a 5% sodium chloride solution (NaCl) at different time intervals.
steel X6CrNiTi18-10 ; corrosion resistance ; salt spray test chamber/NaCl ; time interval ; light microscope
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o izdanju
Povezanost rada
Strojarstvo