3D printing conditions determination for feedstock used in fused filament fabrication (FFF) of 17-4PH stainless steel parts (CROSBI ID 247965)

Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija

Gonzalez-Gutierrez, Joamin ; Godec, Damir ; Guráň, Radoslav ; Spoerk, Martin ; Kukla, Christian ; Holzer, Clemens 3D printing conditions determination for feedstock used in fused filament fabrication (FFF) of 17-4PH stainless steel parts // Metalurgija, 57 (2018), 1/2; 117-120

Podaci o odgovornosti

Gonzalez-Gutierrez, Joamin ; Godec, Damir ; Guráň, Radoslav ; Spoerk, Martin ; Kukla, Christian ; Holzer, Clemens

engleski

3D printing conditions determination for feedstock used in fused filament fabrication (FFF) of 17-4PH stainless steel parts

Fused filament fabrication combined with debinding and sintering could be an economical process for 3D printing of metal parts. In this study, compounding, filament making and FFF processing of a feedstock material containing 55 vol. % of 17-4PH stainless steel powder and a multicomponent binder system are presented. For the FFF process, processing windows of the most significant parameters, such as range of extrusion temperatures (210 to 260 °C), flow rate multipliers (150 to 200 %), and 3D printing speed multipliers (60 to 100 %) were determined for a constant printing bed temperature of 60 °C.

stainless steel, powder, additive manufacturing (AM), FFF, scanning electron microscopy (SEM)

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o izdanju

57 (1/2)

2018.

117-120

objavljeno

0543-5846

1334-2576

Trošak objave rada u otvorenom pristupu

Povezanost rada

Strojarstvo

Poveznice
Indeksiranost