Remineralizing amorphous calcium phosphate based composite resins : The influence of inert fillers on monomer conversion, polymerization shrinkage, and microhardness (CROSBI ID 238952)

Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija

Marović, Danijela ; Šariri, Kristina ; Demoli, Nazif ; Ristić, Mira ; Hiller, Karl-Anton ; Škrtić, Drago ; Rosentritt, Martin ; Schmalz, Gottfried ; Tarle, Zrinka Remineralizing amorphous calcium phosphate based composite resins : The influence of inert fillers on monomer conversion, polymerization shrinkage, and microhardness // Croatian medical journal, 57 (2016), 5; 465-473. doi: 10.3325/cmj.2016.57.465

Podaci o odgovornosti

Marović, Danijela ; Šariri, Kristina ; Demoli, Nazif ; Ristić, Mira ; Hiller, Karl-Anton ; Škrtić, Drago ; Rosentritt, Martin ; Schmalz, Gottfried ; Tarle, Zrinka

engleski

Remineralizing amorphous calcium phosphate based composite resins : The influence of inert fillers on monomer conversion, polymerization shrinkage, and microhardness

The addition of inert fillers to a bioactive dental restorative composite material affects its degree of conversion (DC), polymerization shrinkage (PS), and microhardness (HV). Methods Three amorphous calcium phosphate (ACP)-based composite resins: without added fillers (0-ACP), with 10% of barium-glass fillers (Ba-ACP), and with 10% of silica fillers (Si-ACP), as well as commercial control (Ceram•X, Dentsply DeTrey) were tested in laboratory conditions. The amount of ACP (40%) and the composition of the resin mixture (based on ethoxylated bisphenol A dimethacrylate) was the same for all ACP materials. Fourier transform infrared spectroscopy was used to determine the DC (n = 40), 20 min and 72 h after polymerization. Linear PS and Vickers microhardness (n = 40) were also evaluated. The results were analyzed by paired samples t test, ANOVA, and one-way repeated measures ANOVA with Student-Newman-Keuls or Tukey’s post-hoc test (P = 0.05). Results The addition of barium fillers significantly increased the DC (20 min) (75.84 ± 0.62%) in comparison to 0-ACP (73.92 ± 3.08%), but the addition of silica fillers lowered the DC (71.00 ± 0.57%). Ceram•X had the lowest DC (54.93 ± 1.00%) and linear PS (1.01 ± 0.24%) but the highest HV (20.73 ± 2.09). PS was significantly reduced (P < 0.010) in both Ba-ACP (1.13 ± 0.25%) and Si-ACP (1.17 ± 0.19%) compared to 0-ACP (1.43 ± 0.21%). HV was significantly higher in Si-ACP (12.82 ± 1.30) than in 0-ACP (10.54 ± 0.86) and Ba-ACP (10.75 ± 0.62) (P < 0.010). Conclusion Incorporation of inert fillers to bioactive remineralizing composites enhanced their physical-mechanical performance in laboratory conditions. Both added fillers reduced the PS while maintaining high levels of the DC. Silica fillers additionally moderately improved the HV of ACP composites.

amorphous calcium phosphate ; composite resins ; polymerization shrinkage ; monomer conversion ; microhardness

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o izdanju

57 (5)

2016.

465-473

objavljeno

0353-9504

1332-8166

10.3325/cmj.2016.57.465

Povezanost rada

Kemija

Poveznice
Indeksiranost