Effect of TeO2 Addition on the Mobility of Silver Ions in Ag2O–B2O3–P2O5–TeO2 glasses (CROSBI ID 233753)
Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Moguš-Milanković, Andrea ; Sklepić, Kristina ; Vorokhta, Maryna ; Mošner, Petr ; Koudelka, Ladislav
engleski
Effect of TeO2 Addition on the Mobility of Silver Ions in Ag2O–B2O3–P2O5–TeO2 glasses
The effect of adding TeO2 into (100-x)[0.5Ag2O−0.1B2O3−0.4P2O5]−xTeO2, with 0−80 mol% TeO2 glass on the structural changes and electrical properties has been investigated. DSC and thermodilatomery were used to study their thermal behavior, structure was studied by Raman spectroscopy and electrical properties have been studied over a wide temperature and frequency range by impedance spectroscopy. The addition of the third glass former, TeO2, to the glass network causes the structural transformation from TeO3 (tp) to TeO4 (tbp) which contributes to the changes in conductivity. The glasses with low TeO2 content show only a slow decrease in dc conductivity with addition of TeO2 due to the increase of the number of non-bridging oxygens, which increases the mobility of Ag+ ions. The steep decrease in conductivity for glasses containing more than 40 mol% TeO2 is a result of decrease of the Ag2O content and stronger cross-linkage in glass network through the formation of more Te-eqOax-Te bonds in TeO4 tbp units. The glasses obey scaling of the ac conductivity with respect to temperature indicating that the dynamic process is independent of temperature. However, the scaling of the spectra for different glasses revealed deviations from the Summerfield scaling due to the local structural disorder caused by structural transition in tellurite glass network.
Borophosphate glass ; Silver-ion mobility ; Electrical conductivity
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o izdanju
702
2016.
18-22
objavljeno
1013-9826
1662-9795
10.4028/www.scientific.net/KEM.702.18