Preloščan, Andrija; Vodopivec, Franc; Mamuzić, Ilija
Fine Grained Structural Steel through Controlled Hot Rolling // Sažeci predavanja s 5. međunarodnog simpozija Hrvatskog metalurškog društva "Materijali i metalurgija", tiskano u Metalurgija 41(2002)3 / Mamuzić, Ilija (ur.).
Zagreb: Hrvatsko metalurško društvo, 2002. (poster, međunarodna recenzija, sažetak, znanstveni)


Naslov
Fine Grained Structural Steel through Controlled Hot Rolling

Autori
Preloščan, Andrija ; Vodopivec, Franc ; Mamuzić, Ilija

Vrsta, podvrsta i kategorija rada
Sažeci sa skupova, sažetak, znanstveni

Izvornik
Sažeci predavanja s 5. međunarodnog simpozija Hrvatskog metalurškog društva "Materijali i metalurgija", tiskano u Metalurgija 41(2002)3 / Mamuzić, Ilija - Zagreb : Hrvatsko metalurško društvo, 2002

Skup
5. međunarodni simpozij Hrvatskog metalurškog društva "Materijali i metalurgija"

Mjesto i datum
Šibenik, Hrvatska, 23-27. 06. 2002.

Vrsta sudjelovanja
Poster

Vrsta recenzije
Međunarodna recenzija

Ključne riječi
Structural steel; hot rolling; microstructure

Sažetak
The result on investigation of fine grained structural steel microstructure at hot rolling conditions is given. Billets of 55 mm thickness were heated to 1200 C and rolled starting at this initial temperature to obtain a rolling temperature interval from 1050 C to 760 C. From the rolled plates of 16 mm thickness specimens for optical microscopy were prepared by conventional way. The portions of precipitates of aluminium and niobium carbide were determined using a modified halogen extraction method. The result of the investigation indicates that no grain size decrease could not be expected if the rolling plates are performed significantly below the austenite to ferrite transformation temperature.