Effects of copper and heat treatment parameters on mechanical properties of austempered ductile iron.


Čatipović, Nikša; Živković, Dražen; Dadić Zvonimir
Effects of copper and heat treatment parameters on mechanical properties of austempered ductile iron. // MECHANICAL TECHNOLOGIES AND STRUCTURAL MATERIELS 2016 / Sonja, Jozić ; Branimir, Lela (ur.).
Split: HRVATSKO DRUŠTVO ZA STROJARSKE TEHNOLGIJE, 2016. str. 23-32 (predavanje, međunarodna recenzija, cjeloviti rad (in extenso), znanstveni)


Naslov
Effects of copper and heat treatment parameters on mechanical properties of austempered ductile iron.
(Utjecaj bakra i parametara toplinske obrade na mehanička svojstva izotermički poboljšanog žilavog lijeva.)

Autori
Čatipović, Nikša ; Živković, Dražen ; Dadić Zvonimir

Vrsta, podvrsta i kategorija rada
Radovi u zbornicima skupova, cjeloviti rad (in extenso), znanstveni

Izvornik
MECHANICAL TECHNOLOGIES AND STRUCTURAL MATERIELS 2016 / Sonja, Jozić ; Branimir, Lela - Split : HRVATSKO DRUŠTVO ZA STROJARSKE TEHNOLGIJE, 2016, 23-32

Skup
6th International conference MECHANICAL TECHNOLOGIES AND STRUCTURAL MATERIALS 2016

Mjesto i datum
Split, HRVATSKA, 22.-23. 09.2016

Vrsta sudjelovanja
Predavanje

Vrsta recenzije
Međunarodna recenzija

Ključne riječi
Ductile iron; austempered ductile iron; austempering; microstructure; copper; mechanical properties
(Žilavi lijev; izotermički žilavi lijev; izotermičko poboljšavanje; mikrostruktura; bakar; mehanička svojstva)

Sažetak
In this review papper insight is given how both copper and heat treatment parameters affect mechanical properties of austempered ductile iron (ADI). It has been shown that both copper and other alloying elements such as Ni and Mo affect the mechanical properties of ADI. Also, it has been shown that the strenght, hardness, elongation and fracture toughnes strongly depend on amount of ausferritic ferrite and stable, high carbon enriched retained austenite. The results shown confirm that alloying with Co + Ni produce ductile grades of ADI, while alloying with Cu produce grades of higher strength. The standard processing window depends on the austempering parameters and alloying elements, as well as standard used to produce ADI.

Izvorni jezik
Engleski

Znanstvena područja
Strojarstvo



POVEZANOST RADA


Projekt / tema
069-1201780-2986 - Optimiranje parametara i predviđanje rezultata toplinske obrade metala (Božo Smoljan, )

Ustanove
Fakultet elektrotehnike, strojarstva i brodogradnje, Split