Effects of cold isostatic pressing and granule size distribution on the densification of alumina ceramics
Effects of cold isostatic pressing and granule size distribution on the densification of alumina ceramics // Materialprufung, 57 (2015), 6; 495-498 doi:10.3139/120.110739 (međunarodna recenzija, članak, znanstveni)
CROSBI ID: 762182 Za ispravke kontaktirajte CROSBI podršku putem web obrasca
Naslov
Effects of cold isostatic pressing and granule size distribution on the densification of alumina ceramics
Autori
Ćurković, Lidija ; Majić Renjo, Marijana ; Ciglar, Damir
Izvornik
Materialprufung (0025-5300) 57
(2015), 6;
495-498
Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni
Ključne riječi
Al2O3 ceramics; CIP; densification; shrinkage
Sažetak
In this paper, alumina ceramics was compacted and shaped by cold isostatic pressing. This method provides high-density green compacts, uniformly distributed over the volume, without large pores. Green bodies were sintered at a temperature of 1650 °C. Effects of spray dried granule size distribution and compaction pressure on green and sintered density of alumina was investigated. It was found that green and sintered density slightly increased with increasing compaction pressure and decreased with the increasing alumina granule size. The axial and radial shrinkage of ceramic samples was 20-22 %.
Izvorni jezik
Engleski
Znanstvena područja
Strojarstvo
POVEZANOST RADA
Ustanove:
Fakultet strojarstva i brodogradnje, Zagreb
Citiraj ovu publikaciju:
Časopis indeksira:
- Web of Science Core Collection (WoSCC)
- Science Citation Index Expanded (SCI-EXP)
- SCI-EXP, SSCI i/ili A&HCI
- Scopus